| MF07 Ultra Fine Grade Cemented Carbide
|
| Characteristics |
- ISO K01, USA C4 solid carbide rotary tools
- cobalt content : 7 mass%
- tungsten carbide : 93 mass%
- grain size < 0.6μm
- ultra fine-grained microstructure
- uniform microstructure
|
Mitsubishi Carbide MF07 grade has exceptional advantages
of high
strength and hardness with optimizing high wear resistance
and strong
edge sharpness
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 94.0 |
3.9 |
5.6 |
14.7 |
|
 MF07 |
| Recommended application |
- end mills, micro-drills and routers
- end-milling of die steel
- machining of print circuit boards
|
|
|
| MF10
Ultra Fine Grade Cemented Carbide |
| Characteristics |
- ISO K01, USA C4 solid carbide rotary tools
- cobalt content : 8 mass%
- tungsten carbide : 92 mass%
- grain size < 0.6μm
- ultra fine-grained microstructure
- uniform microstructure
|
Mitsubishi Carbide MF10 grade has exceptional advantages
of high
strength and hardness with optimizing high wear resistance
and strong
edge sharpness.
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 93.8 |
4.0 |
5.8 |
14.6 |
|
 MF10 |
| Recommended application |
- end mills, micro-drills and routers
- end-milling of die steel
- machining of print circuit boards
|
|
|
| MF20
Ultra Fine Grade Cemented Carbide |
| Characteristics |
- ISO K20, USA C2 solid carbide rotary tools
- cobalt content : 12 mass%
- tungsten carbide : 88 mass%
- grain size < 0.6μm
- ultra fine-grained microstructure
- uniform microstructure
|
Mitsubishi Carbide MF20 grade has exceptional advantages
of high
strength and toughness with optimizing high breakage resistance and
strong edge sharpness
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 92.8 |
4.4 |
6.3 |
14.2 |
|
 MF20 |
| Recommended application |
- end mills, micro-drills and routers
- end-milling of die steel, stainless steel and carbon
steel
- machining of print circuit boards
|
|
|
| MF30
Ultra Fine Grade Cemented Carbide |
| Characteristics |
- ISO K30, USA C2 solid carbide rotary tools
- cobalt content : 16 mass%
- tungsten carbide : 84 mass%
- grain size < 0.6μm
- ultra fine-grained microstructure
- uniform microstructure
|
Mitsubishi Carbide MF30 grade has exceptional advantages
of high
strength and toughness with optimizing high breakage resistance and
strong edge sharpness.
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 91.4 |
4.3 |
7.5 |
13.7 |
|
 MF30 |
| Recommended application |
- end mills and routers
- end-milling of die steel, carbon steel, and cast irons
|
|
|
| SF10
Micro Fine Grade Cemented Carbide |
| Characteristics |
- ISO K10, USA C3 solid carbide rotary tools
- cobalt content : 6 mass%
- tungsten carbide : 94 mass%
- grain size < 0.8μm
- micro fine-grained microstructure
- uniform microstructure low content of cobalt
|
Mitsubishi Carbide SF10 grade has exceptional advantages
of high
strength and hardness with optimizing high wear resistance and high
welding resistance.
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 93.5 |
3.8 |
6.6 |
14.9 |
|
 SF10 |
| Recommended application |
- end mills, micro-drills and routers
- end-milling of cast iron, aluminum alloys, other nonferrous
metals and nonmetals
|
|
|
| TF15
Micro Fine Grade Cemented Carbide |
| Characteristics |
- ISO K20, USA C2 solid carbide rotary tools
- cobalt content : 10 mass%
- tungsten carbide : 90 mass%
- grain size < 0.9μm
- micro fine-grained microstructure
- uniform microstructure
|
Mitsubishi Carbide TF15 grade has exceptional advantages
of high
strength and toughness with optimizing high breakage
resistance
sharpness.
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 91.8 |
4.0 |
8.7 |
14.5 |
|
 TF15 |
| Recommended application |
- end mills
- end-milling of die steel, stainless steel, carbon steel,
and cast iron
- machining of print circuit boards
|
|
|
| HTi10
Micro Fine Grade Cemented Carbide |
| Characteristics |
- ISO K10, USA C3 solid carbide rotary tools
- cobalt content : 6 mass%
- tungsten carbide : 94 mass%
- grain size < 1.0μm
- micro fine-grained microstructure
- uniform microstructure
- low content of cobalt
|
Mitsubishi Carbide HTi10 grade has exceptional advantages
of high
strength and hardness with optimizing high welding resistance.
|
Materials properties
| Hardness |
Transverse rupture strength |
Fracture toughness |
Density |
| (HRA) |
(GPa) |
(MPa·m1/2) |
(g/cm3) |
| 92.8 |
3.2 |
6.8 |
14.9 |
|
 HTi10 |
| Recommended application |
- end mills, micro-drills and routers
- end-milling of cast iron, aluminum alloys, other nonferrous
metals and
nonmetals
- machining of print circuit boards
|
|
|